Polycarboxylate Superplasticizer PCE Powder ELT-PC-P

You are here: Home » Product Category » Polycarboxylate Superplasticizer » Polycarboxylate Superplasticizer PCE Powder ELT-PC-P

Polycarboxylate Superplasticizer PCE Powder ELT-PC-P

ELT-PCP is a polycarboxylate based high range water-reducing admixture Powder which enables concrete to be produced with very low water to cement ratios. ELT-PCP does not contain added chlorides and will not promote corrosion in steel.

ELT-PCP is compatible with air-entraining agents, microsilica,accelerators and many other admixtures; however, each material should be added to the concrete separately.

ELT-PCP complies with the requirements of the following standards: ASTM C 494,Type A & F. BS EN 934-2.

Quantity:
Availability:





Inquire Add to Basket

Model:
ELT-PCP
Brand:
ELITE-INDUS

PCE Powder Polycarboxylate Superplasticizer Polycarboxylate Superplasticizer Powder Polycarboxylate Superplasticizer PCE Polycarboxylate Super plasticizer Superplasticizer Polycarboxylate Polycarboxylate based Superplasticizer

Products

Product Description

Polycarboxylate Superplasticizer PCE Powder ELT-PC-P

ELT-PCP is a newest generation polycarboxylate based superplasticizer with Anhui Elite Patent Technology.

ELT-PCP can directly add water diluid to liquid without sedimentation and Cristallisation.

It is white Powder, non- toxic, non-hazardous, and non-corrosive.

ELT-PCP main have two type fine powder, ELT-PCP-A Powder is High range water reducing type, and ELT-PCP-B is slump retention type.

Features of Polycarboxylate Superplasticizer

◆ low dosage, high rate of water reducing

◆ keep concrete good slumption retention

◆ good compatibility with cement

◆ small shrinkage of concrete to keep the stability of volume and durability

◆ environmental in production and usage

Mortar Performance of Polycarboxylate Superplasticizer

◆ It is homologous between water-reducing rate of motar and fluidity of cement paste.

The more fluidity of cement paste, the more water-reducing rate of motar.

◆ Water-reducing rate increases fast and high when the dosage increase.

When the dosage is same,the water-reducing rate of PCE powder is 35% higher than that of other superplasticizer in market.

◆ Due to the influence from the admixture and sand coarse aggregate, Water-reducing rate in concrete is different from that of mortar.

When the the admixture and sand coarse aggregate are in favour of the concrete flow, the water-reducing rate of concrete is higher than that of mortar.

◆ It has antifreezing performance when temperature is above -5℃. So it can be used in antifreezing concrete.

Specification of Polycarboxylate Superplasticizer

◆ Visual appearance: white powder

Density	Solid Content	PH value	Chloridion	Total Alkali
500±15	98±1%	7--9	<0.1%	<5%

◆ Cement Paste Performace

Dosage (%)	5 min	1 Hour	Fluidity Loss(%)
0.12	140	160	0
0.14	160	180	0
0.16	180	200	0
0.18	200	240	0
0.20	240	270	0
0.22	270	310	0
Powder Dosage (%)		(%) water-reducing rate
0.14		18
0.18		23
0.20		29
0.22		32

◆ It makes cement good dispersibility and fluidity in low dosage.

◆ When dosage is from 0.12% to 0.22%, the cement paste fluidity grows obviously.

◆ There is no loss of fluidity within 1 hour in cement paste.

◆ The fluidity of PCE powder is 2 times of other superplasticizer in market.

Recommend Dosage of Polycarboxylate Superplasticizer

The recommend dosage of superplasticizer for concrete: 0.1-0.25% base on cement quantity.

Solid contents of PCE powder is 98%. Normal dosage is 0.12%-0.3%.

◆ when dosage is 0.06%, it has 12% water reducing rate and 23% strength growth, this beyond the performance of common pumping agent in market.

◆ when dosage is 0.1%, performance beyond that of PNS and Melamine. But when dosage is below 0.14%, its good performance is not obvious.

◆ When dosage is above 0.20%, it is excellent in concrete fluidity and pumping performance. Therefore, the best dosage is recommended as 0.12-0.24%;

◆ when making concrete with high grade, big dosage of fly ash or superfine slag powder or other special requirements, dosage can be expanded to 0.3-0.5%. Test state that there is no cohesion and bleeding in concrete even the dosage expand to 0.5%, and its water-reducing rate still increase . But air content increase, setting delay, strength decrease.

Certificate Of Analysis of Polycarboxylate Superplasticizer

◆ ELT-PCP-A

Homogeneity Index
Item	Qualification	Item	Qualification
Appearance	Powder	Cement Fluidity mm	274
PH Value	7-9	Solid Content	97+/-1
Index Of Concrete With Admixture
Item	Top Grade of National Standard		Test Result
Ratio Of Bleeding Rate	≤60		7
Water Reducing Rate	≥25		35
Air Content	≤6		1.5
Condensation time difference	Initial Set	-90 to +120	+50
Condensation time difference	Final Set		+35
Ratio of Compressive strength	1d	≥170	177
	3d	≥160	168
	7d	≥150	159
	28d	≥130	142
Ratio of Shrink	28d	≤100	95
Test Method : GB8076-2008

◆ ELT-PCP-B

Homogeneity Index
Item	Qualification	Item	Qualification
Appearance	Powder	Cement Fluidity mm	268
PH Value	7-9	Solid Content	97+/-1
Index Of Concrete With Admixture
Item	Top Grade of National Standard		Test Result
Ratio Of Bleeding Rate	≤60		7
Water Reducing Rate	≥25		33
Air Content	≤6		1.5
Condensation time difference	Initial Set	-90 to +120	+50
Condensation time difference	Final Set		+35
Ratio of Compressive strength	1d	≥170	176
	3d	≥160	165
	7d	≥150	155
	28d	≥130	140
Ratio of Shrink	28d	≤100	95
Test Method:GB8076-2008