Macro Synthetic Fiber Twist 54MM

Macro Synthetic Fiber twist is a 100% virgin blended polymer synthetic Structural macrofiber successfully used as an alternate to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications. Macro synthetic fiber twisted was made of a strong synthetic copolymer, to increase load-transfer and post-crack performance.

Quantity:
Availability:





Inquire Add to Basket

Model:
ELT-Twist
Brand:
ELITE-INDUS

Macro Synthetic Fiber Synthetic macrofiber synthetic macro fiber synthetic macro fiber 54mm synthetic macro fiber hybrid Macro Synthetic Fiber 54mm pp fiber twisted polypropylene fiber twisted

Products

Product Description

Macro Synthetic Fiber Twist 54MM

Macro Synthetic Fiber Twist comply with ASTM C1116 and EN14889-2 Standard Specification for Fiber Reinforced Concrete and Shotcrete, and are specifically used for the reduction of plastic shrinkage cracks, to improve impact, shatter and abrasion resistance, to increase fatigue resistance, to increase toughness of concrete and provide long term durability of concrete, structural enhancements and cement based building products.

Functions of Macro Synthetic Fiber Twist

◆ Increases impact, shatter and abrasion resistance of concrete

◆ Reduces segregation, plastic settlement, and shrinkage cracking of concrete

◆ Provides three-dimensional reinforcement against macro-cracking

◆ Increases overall durability, fatigue resistance and flexural toughness

◆ Reduction of in-place cost versus wire mesh for temperature / shrinkage crack control

◆ Easily added to concrete mixture at any time prior to placement

Applications of Macro Synthetic Fiber Twist

◆ Industrial and residential flooring

◆ Whitetoppings, bridge decks and pavements

◆ Thin walled pre-cast (septic tanks, vaults, walls, etc.)

◆ Mass concrete

Specifications of Macro Synthetic Fiber Twist

Density (g/cm 3)	0.91 +/- 0.01	Equivalent Dia. (mm)	0.3±0.05
Shape	Twist	break tensile Ratio (%)	8-15
Crack Ratio (%)	20+/-5	Melting point ( C. Deg)	160-170
Tensile Strength (Mpa)	500 to 800	Water Absorption	Negligible
Elastic Modulus (Mpa)	>3500	Resistance to acid & alkali	Excellent
Material	Virgin Copolymer/Polypropylene
Length (mm)	38/48 /54 or as per your request
Dosage rates will vary depending upon the reinforcing requirements and can range from 1kg/m³ to 6 kg/m³

Directions for Use

◆ Macro Synthetic Fiber ELT-Twist can be added to the concrete mixture at any time prior to placement of the concrete.

◆ Macro Synthetic Fiber ELT-Twist is generally recommended to add any fiber material at the ready-mix concrete plant during batching. Fibers must be mixed with concrete for a minimum of three to five minutes at maximum mixing speed, depending on the mixer type, to ensure complete dispersion and uniformity.

Packing

Shape	Inner Packing (PE Film Bag)	Outer Packing (Plastic Woven Bag)	20’gp	40’HQ
Twist	0.5/1.0kg	10kg	5500kg	13000kg
	Inner Packing(Water Soluble Paper Bag)	Outer Packing (Carton)
	0.5/1.0kg	10kg	4000kg	9600kg
Other Packing Can As Per Your Request